PowerSteel.eu Aerospace steel 1.4542 / X5CrNiCuNb16-4 P1070, H1025, H1150, H1150D

1.4542 / X5CrNiCuNb16-4 P1070, H1025, H1150, H1150D

Round Bars 6–230 mm
Tensile Strength Rm:
from 860 MPa
Yield Strength:
Working temperature:
Equivalent or similar:
AFNOR Z3CNDA13.8, UNS S13800, DIN X3CrNiMoAl13-8-2

About material

1.4542 / X5CrNiCuNb16-4 solution annealed

1.4542 / X5CrNiCuNb16-4 hardened P1070, H1025, H1150, H1150D

17-4PH is a well-established precipitation hardening martensitic stainless steel capable of achieving very high strength and hardness after a relatively simple heat treatment. It offers excellent corrosion resistance combined with a structured range of mechanical property levels depending on the precise heat treatment applied.

The materials can be readily machined and fabricated in the softer tempers and can then be heat-treated to exceptional strength and dimensional stability. 17-4PH is widely used in the chemical, petrochemical, offshore, paper, and aerospace industries making best use of its outstanding corrosion resistance, wear resistance, strength and hardness.